Disgrifiad Cynnyrch
Tiwbiau Mecanyddol Di-dor JIS G3445 Dur Carbon
Pam mae gan bibell ddur di-dor dur carbon JIS G3445 fantais ym maes peiriannau?
1. Mae'r deunydd pibell ddur o dan safon JIS G3445 yn ddur carbon isel yn bennaf, megis y gyfres STKM11A/STKM13, gyda chyfwerth carbon weldio (CE) o<0.35%, which can be welded without preheating, which can significantly reduce the processing cost. Compared with the same grade of carbon steel pipe, the cost is about 25% lower than ASTM A106 (because the high-temperature performance testing cost is saved).
2. STKM12C yw'r dewis deunydd gorau ar gyfer silindrau hydrolig. Mae goddefgarwch pibell ddur di-dor dur carbon JIS G3445 yn cael ei reoli ar ±0.15mm trwy'r broses dynnu oer, tra bod angen malu ychwanegol ar ASTM A53 o dan yr un dechnoleg prosesu. Mae JIS G3445 wedi dod yn ddewis cost-effeithiol ar gyfer cyrff silindr hydrolig Llai na neu'n hafal i 32MPa gyda'i broses lluniadu oer manwl gywir.
3. Mae pibell di-dor dur carbon JIS G3445 yn cefnogi prosesu dwfn fel stampio a phlygu, a gellir ei ddefnyddio ar gyfer cromfachau siasi a ffurfio ffrâm corff automobiles.
Ceisiadau
Mae Tiwb Mecanyddol Di-dor Dur Carbon JIS G3445 yn addas ar gyfer ystod eang o gymwysiadau ar draws ystod eang o ddiwydiannau. Mae'r ceisiadau hyn yn cynnwys:
- Rhannau modurol:systemau atal, colofnau llywio, siafftiau gyrru a chydrannau strwythurol eraill.
- Rhannau peiriannau:fframiau, siafftiau a gerau.
- Offer adeiladu:bŵmiau craen, cydrannau pontydd a rhaglenni -dyletswydd trwm eraill.
- Peirianneg gyffredinol:fframiau strwythurol, systemau cludo a chymwysiadau mecanyddol eraill.
Cyfansoddiad Cemegol
| Gradd Dur | Cyfansoddiad Cemegol | |||
| STKM 11A | C: 0.12% max, Si: 0.35% max, Mn: 0.60% max, P: 0.040% max, S: 0.040% max | |||
| STKM 12A | C: 0.20% max, Si: 0.35% max, Mn: 0.60% max, P: 0.040% max, S: 0.040% max | |||
| STKM 12B | C: 0.20% max, Si: 0.35% max, Mn: 0.60% max, P: 0.040% max, S: 0.040% max | |||
| STKM 12C | C: 0.20% max, Si: 0.35% max, Mn: 0.60% max, P: 0.040% max, S: 0.040% max | |||
| STKM 13A | C: 0.25% max, Si: 0.35% max, Mn: 0.30-0.90%, P: 0.040% max, S: 0.040% max | |||
| STKM 13B | C: 0.25% max, Si: 0.35% max, Mn: 0.30-0.90%, P: 0.040% max, S: 0.040% max | |||
| STKM 13C | C: 0.25% max, Si: 0.35% max, Mn: 0.30-0.90%, P: 0.040% max, S: 0.040% max | |||
| STKM 15A | C: 0.25% max, Si: 0.35% max, Mn: 1.30% max, P: 0.040% max, S: 0.040% max | |||
Priodweddau Mecanyddol
| Gradd Dur | Cryfder Tynnol (MPa) | Cryfder Cynnyrch (MPa) | elongation(%) |
| STKM 11A | 290 mun | 180 mun | 25 mun |
| STKM 12A | 345 mun | 175 mun | 35 mun |
| STKM 12B | 390 mun | 275 mun | 25 mun |
| STKM 12C | 470 mun | 355 mun | 20 mun |
| STKM 13A | 375 mun | 215 mun | 30 mun |
| STKM 13B | 440 mun | 305 mun | 20 mun |
| STKM 13C | 510 mun | 375 mun | 20 mun |
| STKM 15A | 470 mun | 345 mun | 20 mun |
Graddau Amgen Posibl
Er bod JIS G3445 yn nodi ystod gynhwysfawr o diwbiau mecanyddol di-dor dur carbon, mae graddau amgen ar gael mewn safonau rhyngwladol eraill. Rhai dewisiadau amgen posibl i'w hystyried yw ASTM A519, DIN 2391, a BS 6323.
Mae'n hanfodol ymgynghori â'r safonau perthnasol a chymharu priodweddau a manylebau deunyddiau wrth ystyried graddau amgen ar gyfer cymwysiadau penodol.
Pecynnu
Unwaith y bydd y pibellau wedi pasio'r holl archwiliadau a phrofion, maent yn barod i'w pecynnu. Maent fel arfer yn cael eu pecynnu mewn byrnau wedi'u lapio mewn plastig. Gellir bwndelu'r pibellau ac yn barod i'w danfon yn unol â gofynion y cwsmer, gan sicrhau bod y pibellau yn cael eu diogelu wrth eu cludo ac yn atal difrod i'r wyneb.
Sioe Cynhyrchion
Tagiau poblogaidd: jis g3445 dur carbon tiwbiau mecanyddol di-dor, Tsieina, cyflenwyr, gweithgynhyrchwyr, ffatri, addasu, cyfanwerthu, pris, OEM, melin, cynhyrchydd, ar werth